Plasma display apparatus, fluorescent material, and fluorescent material manufacturing method

ABSTRACT

The present invention aims to inhibit water adsorption onto the surface of a blue phosphor(blue fluorescent material), decrease luminance degradation and chromaticity shift of a phosphor, or improve discharge characteristics thereof. Used in a phosphor for a plasma display is a blue phosphor in which trivalent Eu ions substitute for part of divalent Eu ions. This substitution eliminates oxygen vacancy in the vicinity of layers containing Ba atoms (Ba—O layers) in the blue phosphor, and thus inhibits water adsorption onto the surface of the blue phosphor, decreases luminance degradation and chromaticity shift of the phosphor, or improves discharge characteristics thereof.

TECHNICAL FIELD

The present invention relates to a plasma display apparatus(device) used for image display on a television or other equipment. It also relates to a phosphor for use in the plasma display device, and a method of fabricating the phosphor(fluorescent material).

BACKGROUND ART

Among color display devices used for image display on a computer or television, a display device using a plasma display panel (hereinafter referred to as a “PDP”) has recently been drawing attention, as a large, thin, and light color display device.

A plasma display device using a PDP performs additive color mixing of so-called three primary colors (red, green, and blue) to provide full-color display. For this full-color display, a plasma display device has phosphor layers for emitting the respective three primary colors, i.e. red (R), green (G), and blue (B). Phosphor particles constituting these phosphor layers are exited by ultraviolet light generated in discharge cells of the PDP to generate visible light of respective colors.

Known as compounds used for the phosphors of above respective colors are (Y, Gd)BO₃:Eu³⁺ and Y₂O₃:Eu³⁺ for red emission, Zn₂SiO₄:Mn²⁺ for green emission, and BaMgAl₁₀O₁₇:Eu²⁺ for blue emission. Each of these phosphors is fabricated by mixing specific materials and firing the mixture at high temperatures of at least 1,000° C. for solid-phase reaction (see “Phosphor Handbook” p. 219 and 225, Ohm-sha, for example). The phosphor particles obtained by this firing are used after they are milled and classified (average diameter of red and green particles: 2 to 5 μm, average diameter of blue particles: 3 to 10 μm).

The phosphor particles are milled and classified for the following reason. In general, when phosphor layers are formed on a PDP, a technique of screen-printing a paste of phosphor particles of each color is used. In application of the paste, the smaller and more uniform diameters of phosphor particles (i.e. a uniform particle size distribution) can easily provide the smoother coated surface.

In other words, when phosphor particles have smaller and more uniform diameters and shapes approximating to a sphere, the coated surface is smoother. The smoother coated surface increases the packing density of the phosphor particles in a phosphor layer and the emission surface area of the particles, thus alleviating unstableness at address drive. As a result, it is theoretically considered that the luminance of the plasma display device can be increased.

However, the smaller diameters of the phosphor particles increase the surface area of the phosphor and defects of the phosphor. For this reason, a large quantity of water, carbonic acid gas, or organic substances including hydrocarbon are prone to adhere to the surface of the phosphor. Especially for a blue phosphor in which divalent Eu ions mainly emit light, such as Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), each of these crystal structures has a layer structure (see “Display and Imaging”, 1999, vol. 7, pp 225–234, for example). In these layers, there is oxygen (O) vacancy in the vicinity of layers containing Ba atoms (Ba—O layers) for any particle size. This fact poses a problem: when the particle size is smaller, the amount of defects further increases. (see OYO BUTSURI (Applied Physics), vol. 70, No. 3, 2001, pp 310, for example).

For this reason, water existing in air is selectively adsorbed onto the surface of the Ba—O layer of the phosphor. Therefore, because a large quantity of water is released into a panel in a panel manufacturing process, the water reacts with the phosphor and MgO during discharge. This poses problems of luminance degradation and chromaticity shift (color shift or image burn caused by the chromaticity shift), or decrease in drive voltage margin and increase in discharge voltage. A conventionally devised method to address these problems is coating the entire surface of the phosphor with a crystal of Al₂O₃, in order to recover the defects in the vicinity of the Ba—O layer (see Japanese Patent Unexamined Publication No. 2001-55567, for example).

However, this method poses another problem: coating the entire surface causes absorption of ultraviolet light and thus decreases the emission luminance of the phosphor, and the ultraviolet light decreases the luminance.

DISCLOSURE OF THE INVENTION

In order to address these problems, the present invention aims to inhibit water adsorption onto the surface of a blue phosphor, decrease luminance degradation and chromaticity shift of a phosphor, or improve discharge characteristics thereof. Especially in the present invention, elimination of oxygen vacancy in the vicinity of a layers containing Ba atoms (Ba—O layers) in a blue phosphor inhibits water adsorption onto the surface of the blue phosphor, decreases luminance degradation and chromaticity shift of a phosphor, or improves discharge characteristics thereof.

In order to accomplish the object, in the present invention, elimination of oxygen vacancy in the vicinity of layers containing Ba atoms (Ba—O layers) in a blue phosphor inhibits water adsorption onto the surface of the blue phosphor, decreases luminance degradation and chromaticity shift of a phosphor, or improves discharge characteristics thereof.

A plasma display device of the present invention has a plasma display panel in which a plurality of discharge cells of one or a plurality of colors are disposed in arrays, phosphor layers having a color corresponding to the respective discharge cells are disposed, and the phosphor layers are excited by ultraviolet light to emit light. The phosphor layers have a blue phosphor. The blue phosphor is made of a compound represented by Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) or Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x) in which trivalent Eu ions substitutes for part of divalent Eu ions.

A phosphor of the present invention includes a blue phosphor that is made of a crystal structure of Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) or Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇: Eu_(x) and exited by ultraviolet light to emit visible light. In the blue phosphor, part of divalent Eu ions constituting the phosphor is made trivalent.

A method of manufacturing a phosphor of the present invention includes firing a blue phosphor having divalent Eu ions as its matrix, i.e. Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) or Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x,) in an oxidizing atmosphere, to make part of the divalent Eu ions trivalent.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a plan view of a plasma display panel, (PDP) in accordance with one embodiment of the present invention with a front glass substrate thereof removed.

FIG. 2 is a perspective view showing a partial section of a structure of an image display area of the PDP.

FIG. 3 is a block diagram of a plasma display device in accordance with one embodiment of the present invention.

FIG. 4 is a sectional view of an image display area of a PDP in accordance with one embodiment of the present invention.

FIG. 5 is a schematic diagram showing a structure of an ink dispenser used when phosphor layers of the PDP is formed.

FIG. 6 is a schematic diagram showing an atomic structure of a blue phosphor in accordance with one embodiment of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENT

First, a description is provided of an advantage of eliminating oxygen vacancy in the vicinity of a Ba—O layer in a blue phosphor.

A phosphor for use in a PDP or other equipment is fabricated by a solid-phase reaction method, an aqueous solution reaction method, or other methods. When a phosphor has smaller particle diameters, defects are likely to occur. Especially for the solid-phase reaction method, it is known that milling a phosphor after firing leads many defects. It is also known that ultraviolet light having a wavelength of 147 nm generated by discharge in driving a panel causes defects in a phosphor (see Electronic Information and Communication Institute, Technical Research Report, EID99-94, Jan. 27, 2000, for example).

Especially for BaMaAl₁₀O₁₇:Eu_(x,) a blue phosphor, it is known that the phosphor itself has oxygen vacancy especially in a Ba—O layer thereof (see OYO BUTSURI (Applied Physics) vol. 70, No. 3, 2001, pp 310, for example).

FIG. 6 is a diagram schematically showing a structure of a Ba—O layer in the blue phosphor BaMgAl₁₀O₁₇:Eu

For a conventional blue phosphor, existence of these defects itself has been considered as a cause of luminance degradation. In other words, it has been considered the degradation is caused by defects. Such defects are caused by impact of ions generated in driving a panel on the phosphor and by ultraviolet light having a wavelength of 147 nm.

The inventors have found that the luminance degradation is not only essentially caused by existence of the defects but is caused by selective adsorption of water or carbonic acid gas to oxygen (O) vacancy in the vicinity of a Ba—O layer. By irradiating the adsorption with ultraviolet light or ions, the phosphor reacts with water, thus causing luminance degradation and color shift. In other words, the inventors have come to know that adsorption of water or carbonic acid gas to oxygen vacancy in the vicinity of a Ba—O layer in a blue phosphor causes a various kinds of degradation.

Based on this knowledge, the inventors have decreased oxygen vacancy in the vicinity of a Ba—O layer in a blue phosphor to prevent degradation thereof in a panel manufacturing process and in driving a panel, without decreasing the luminance of the blue phosphor.

In order to decrease the oxygen vacancy in the vicinity of Ba—O layers, the inventors have substituted trivalent Eu ions for part of divalent Eu ions substituting for the element Ba in a blue phosphor having a crystal structure of BaMgAl₁₀O₁₇:Eu or BaSrMgAl₁₀O₁₇:Eu.

Now, a description is provided of an advantage of substituting trivalent Eu ions for part of divalent Eu ions in BaMgAl₁₀O₁₇:Eu

The element Eu (europium) in BaMgAl₁₀O₁₇, a blue phosphor, enters into the lattice of Ba and exists as divalent positive ions. When trivalent Eu ions substitute for part of the divalent ions, positive electrical charges increase in the crystal. In order to neutralize these positive electrical charges (compensate for electrical charges), negatively charged oxygen compensates for the oxygen vacancy in the vicinity of the element Ba. As a result, it is considered that the oxygen vacancy in the vicinity of the Ba—O layers can be decreased.

Methods of manufacturing a phosphor of the present invention are described hereinafter. Methods of manufacturing a phosphor itself include a conventional solid-phase firing method, a liquid-phase method, and a liquid spray method. In the solid-phase firing method, oxide or carbonate materials are fired using a fluxing agent. In the liquid-phase method, a precursor of a phosphor is fabricated, using a co-precipitation method of hydrolyzing organometallic salts or nitrates in an aqueous solution or forming precipitation by addition of an alkali, and then the precursor is heat-treated. In the liquid spray method, an aqueous solution containing phosphor materials is sprayed into a high-temperature furnace. It has been found that substituting trivalent ions for part of divalent ions of Eu in BaMgAl₁₀O₁₇:Eu is effective, in a phosphor fabricated by any method described above.

Now, as an example of a method of fabricating a phosphor, a description is provided of preparation of a blue phosphor by a solid-phase reaction method. Carbonates and oxides, such as BaCO₃, MgCO₃, Al₂O₃, and Eu₂O₃, as materials, are mixed with a small amount of fluxing agent (AlF3 or BaCl₂), as a sintering agent. The mixture is fired at a temperature of 1,400° C. for two hours. Then, the fired mixture is milled and classified. Next, the milled and classified product is fired at a temperature of 1,500° C. for two hours in a reducing atmosphere (H₂(5%)-N₂ matrix) and milled and classified again, to provide a phosphor.

Next, the phosphor is fired in an oxidizing atmosphere, i.e. oxygen (O₂), oxygen (O₂)-nitrogen (N₂), or ozone (O₃)-nitrogen (N₂), at temperatures ranging from 350 to 900° C., to make part of divalent Eu ions trivalent.

When a phosphor is fabricated from an aqueous solution (liquid-phase method), organometallic salts containing elements constituting the phosphor, such as alkoxide and acetylacetone, or nitrates are dissolved in water, and then a co-precipitate (hydrate) is obtained by hydrolysis. The hydrate is hydro-thermally synthesized (crystallized in an autoclave), fired in air, or sprayed into a high-temperature furnace to provide fine particles. The fine particles are fired at a temperature of 1,500° C. for two hours in a reducing atmosphere (H₂(5%)-N₂ matrix) to provide a phosphor.

Next, the product obtained by this method is fired in O₂, O₂—N₂, or O₃—N₂ at temperatures ranging from 350 to 900° C., to provide a phosphor.

It is desirable that the amount of trivalent Eu ions with respect to the amount of divalent Eu ions ranges from 0.01 to 15%. For a substitution value up to 0.01%, prevention of luminance degradation is ineffective. For a substitution value of at least 15%, the luminance of the phosphor decreases and trivalent Eu ions cause red emission; thus, it is not preferable. It has been recognized that part of divalent Eu ions has made trivalent by measurement of an emission intensity ratio using cathode luminescence (CL), i.e. an intensity ratio of blue emission of divalent Eu ions (450 nm) to red emission of trivalent Eu ions (620 nm).

In this manner, substituting trivalent Eu ions for divalent Eu ions in a crystal of BaMgAl₁₀O₁₇:Eu by the conventional method of fabricating blue phosphor particles can provide a blue phosphor resistant to water (i.e. durable against water and carbonic acid gas generated in a phosphor firing process, panel sealing process, panel aging process, or in driving a panel), without causing degradation of the luminance of the blue phosphor.

A plasma display device of the present invention has a PDP in which a plurality of discharge cells of one or a plurality of colors are disposed in arrays, phosphor layers having a color corresponding to the respective discharge cells are disposed, and the phosphor layers are excited by ultraviolet light to emit light. Each of the blue phosphor layers is characterized by being made of blue phosphor particles in which trivalent Eu ions substitute for part of divalent Eu ions in a crystal of BaMgAl₁₀O₁₇:Eu or BaSrMgAl₁₀O₁₇:Eu_(x) that has uniform particle size distribution.

The diameters of blue phosphor particles in which trivalent Eu ions substitute for part of divalent Eu ions in BaMgAl₁₀O₁₇:Eu or BaSrMgAl₁₀O₁₇:Eu are as small as 0.05 to 3 μm. The particle size distribution of the blue particles is excellent. Further, when each of phosphor particles forming a phosphor layer has a spherical shape, the packing density of the layer increases. This increases the emission area of phosphor particles substantially contributing to light emission. The increased emission area can increase the luminance of a plasma display device and provide a plasma display device that has inhibited luminance degradation and color shift and excellent luminance characteristics.

Now, it is more preferable that the average particle diameter of phosphor particles ranges from 0.1 to 2.0 μm. As to the particle size distribution, it is more preferable that the maximum particle size is at most four times of the mean value and the minimum value is at least a quarter of the mean value. In a phosphor particle, the area ultraviolet light reaches is as shallow as several hundred nm from the surface of the particle and only the surface thereof emits light. When the diameter of such a phosphor particle is 2.0 μm or smaller, the surface area of the particle contributing to light emission increases and the emission efficiency of the phosphor layer is kept high. For a diameter of at least 3.0 μm, the thickness of the phosphor must be at least 20 μm and a sufficient discharge space cannot be ensured. For a diameter up to 0.1 μm, defects are likely to occur and the luminance does not increase.

When the thickness of a phosphor layer is set to 8 to 25 times of the average diameter of phosphor particles, a sufficient discharge space can be ensured while the emission efficiency of the phosphor layer is kept high. Therefore, the luminance of a plasma display device can be increased. Especially when the average particle diameter of a phosphor is up to 3 μm, this effect is greater (see The Institute of Image Information and Television Engineers, IDY2000-317, pp 32).

A specific example of phosphor particles used for blue phosphor layers in a plasma display device is made of a compound represented by Ba_(1−x)MgAl₁₀O₁₇:Eu, or Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x.) When values X and Y in these compounds are such that 0.03≦X≦0.20 and 0.1≦Y≦0.5, the blue phosphor layers have a high luminance. Thus, satisfying these conditions is preferable.

A specific example of phosphor particles used for red phosphor layers in a plasma display device is made of a compound represented by Y_(2−x)O₃:Eu_(x) or (Y,Gd)_(1−x)BO₃:Eu_(x.) When value X in the compounds of the red phosphor is such that 0.05≦X≦0.20, the red phosphor layers have an excellent luminance and resistance to luminance degradation. Thus, satisfying this condition is preferable.

A specific example of phosphor particles used for green phosphor layers in a plasma display device is made of a compound represented by Ba_(1−x)Al₁₂O₁₉:Mn_(x) or Zn_(2−x)SiO₄:Mn_(x.) When value X in the compounds of the green phosphor is such that 0.01≦X≦0.10, the green phosphor layers have an excellent luminance and resistance to luminance degradation. Thus, satisfying this condition is preferable.

A method of manufacturing a PDP of the present invention is characterized by having a disposing step, firing step and sealing step. In the disposing step, pastes are disposed on a substrate of a first panel. Each kind of the pastes is made of blue phosphor particles in which trivalent Eu ions substitute for part of divalent Eu ions in the blue phosphor Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) or Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), red phosphor particles, or green phosphor particles, and a binder. In the firing step, the binder included in each kind of the pastes disposed on the first panel is burnt out. In the sealing step, the first panel having the phosphor particles disposed on the substrate by the firing step, and a second panel are placed one on the other, and sealed together. These steps can provide a PDP having excellent luminance and resistance to luminance degradation.

The phosphor of the present invention can also be applied to fluorescent lighting. Such fluorescent lighting of the present invention has a phosphor layer that is excited by ultraviolet light to emit visible light. The phosphor layer is characterized by being made of phosphor particles in which trivalent Eu substitutes for part of divalent Eu in a blue phosphor thereof. This structure can provide fluorescent lighting that has phosphor particles having excellent light emission characteristics, luminance, and resistance to luminance degradation.

A plasma display device in accordance with one embodiment of the present invention is described hereinafter with reference to the accompanying drawings.

FIG. 1 is a schematic plan view of a PDP with a front glass substrate thereof removed. FIG. 2 is a partially sectional view in perspective of an image display area of the PDP. In FIG. 1, the number of display electrodes, display scan electrodes, and address electrodes is reduced to facilitate explanation. With reference to these FIGS. 1 and 2, the structure of a PDP is described.

As shown in FIG. 1, PDP 100 includes front glass substrate 101 (not shown), rear glass substrate 102, N display electrodes 103, N display scan electrodes 104 (Nth electrode indicated by N), M address electrodes 107 (Mth electrode indicated by M), and hermetic seal layer 121 shown by oblique lines. The PDP has an electrode matrix having a three-electrode structure made of respective electrodes 103, 104, and 107. Respective cells are formed at the respective intersections of display scan electrodes 104 and address electrodes 107. Also, the reference character 123 refers to a dielectric glass layer.

As shown in FIG. 2, this PDP 100 is structured so that a front panel and a rear panel are assembled together and discharge space 122 formed between the front panel and the rear panel is filled with a discharge gas. In the front panel, display electrodes 103, display scan electrodes 104, dielectric glass layer 105, and MgO protective layer 106 are disposed on a principal surface of front glass substrate 101. In the rear panel, address electrodes 107, dielectric glass layer 108, barrier ribs 109, and phosphor layers 110R, 110G and 110B are disposed on a principal surface of rear glass substrate 102. In phosphor layers 110B, trivalent Eu ions substitute for divalent Eu ions.

When an image is displayed on a plasma display device, first, display driver circuit 153, display scan driver circuit 154, and address driver circuit 155 are connected to PDP 100, as shown FIG 3. Next, according to control of controller 152, a signal voltage is applied across display scan electrode 104 and address electrode 107 of a cell to be lit for address discharge therebetween. Then, a pulse voltage is applied across display electrode 103 and display scan electrode 104 for sustain discharge. This sustain discharge generates ultraviolet light in the cell. The phosphor layer excited by this ultraviolet light emits light, thus lighting the cell. Combination of lit and unlit cells of the respective colors provides image display. Also, in FIG. 3, the reference character 150 refers to a PDP drive unit and the reference character 160 refers to a PDP.

Next, a method of manufacturing this PDP 100 is described with reference to FIGS. 4 and 5.

(1) Production of Front Panel

First, N display electrodes 103 and N display scan electrodes 104 are arranged on front glass substrate 101 alternately, in parallel with each other, like stripes. (In FIG. 2, only two of respective electrodes are shown for simplicity.) Thereafter, the electrodes are covered with dielectric glass layer 105, and MgO protective layer 106 is further formed over the surface of dielectric glass layer 105.

Display electrodes 103 and display scan electrodes 104 are made of silver. These electrodes are formed by applying a silver paste for electrodes by screen-printing and firing the paste.

Dielectric glass layer 105 is formed by applying a paste containing lead glass material by screen-printing, and firing the paste at a specified temperature for a specified period of time (e.g. at 56° C. for 20 min.) so that the layer has a specified thickness (approx. 20 μm). Examples of the paste containing lead glass material to be used include a mixture of PbO (70 wt %), B₂O₃ (15 wt %), SiO₂ (10 wt %), Al₂O₃ (5 wt %) and an organic binder (α-terpineol containing 10% of ethyl cellulose dissolved therein).

The organic binder contains a resin dissolved in an organic solvent. Acrylic resin can be used as a resin other than the ethyl cellulose, and n-butylcarbitol as an organic solvent. Further, a dispersion agent (e.g. glyceryl trileate) can be mixed into such an organic binder.

MgO protective layer 106 is made of magnesium oxide (MgO). The layer is formed by sputtering method or chemical vapor deposition (CVD) method, for example, to have a specified thickness (approx. 0.5 μm).

(2) Production of Rear Panel

First, M address electrodes 107 are formed in lines by screen-printing a silver paste for electrodes on rear glass substrate 102 and firing the paste. Next, dielectric glass layer 108 is formed by applying a paste containing lead glass material to the address electrodes by a screen-printing method. Barrier ribs 109 are formed by repeatedly applying the same paste containing lead glass material to the dielectric glass layer by the screen-printing method at a specified pitch and firing the paste. These barrier ribs 109 partition discharge space 122 into respective cells (unit emission area) in the direction of the lines.

FIG. 4 is a partially sectional view of PDP 100. As shown in the drawing, interval dimension W between barrier ribs 109 is specified to a value ranging from approx. 130 to 240 μm, according to a HDTV screen having a diagonal size ranging from 32 to 50 in.

Paste-like phosphor ink made of red (R), green (G), or blue (B) phosphor particles and an organic binder is applied to grooves between barrier ribs 109, and fired at temperatures ranging from 400 to 590° C. to burn out the organic binder. Thus, phosphor layers 110R, 110G, and 110B in which phosphor particles of corresponding colors are bound are formed. In the blue phosphor particles, trivalent Eu ions substitute for part of divalent Eu ions in Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) or Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x.)

It is preferable that thickness L of each of these phosphor layers 110R, 110G, and 110B on address electrode 107 in the direction of lamination is approx. 8 to 25 times of the average diameter of the phosphor particles of each color. In other words, in order to ensure a certain luminance (emission efficiency) when a phosphor layer is irradiated with a specified amount of ultraviolet light, the phosphor layer needs to absorb ultraviolet light generated in the discharge space instead of allowing it to pass through. For this purpose, it is desirable that the phosphor layer has a thickness in which at least eight layers, preferably, approx. 20 layers are laminated. For a thickness larger than that, the emission efficiency of the phosphor layer is almost saturated. Further, for a thickness exceeding lamination of approx. 20 layers, sufficiently large discharge space 122 cannot be ensured.

Phosphor particles having sufficiently small diameters and spherical shapes, like those obtained by hydrothermal synthesis or other methods, have a packing factor of the phosphor layer and a total surface area of the phosphor particles larger than those of phosphor particles having non-spherical shapes, even when the number of laminated layers are the same. As a result, for phosphor particles having spherical shapes, the surface area thereof contributing to actual light emission of the phosphor layer is increased and the emission efficiency is further increased. Descriptions are provided later of a method of synthesizing these phosphor layers 110R, 110G, and 110B, and a method of fabricating blue phosphor particles for use in the blue phosphor layer in which trivalent Eu ions substitute for divalent Eu ions.

(3) Production of PDP by Assembly Panels

The front panel and the rear panel produced in this manner are placed one on the other so that respective electrodes on the front panel are orthogonal to the address electrodes on the rear panel. A sealing glass is inserted between the panels in the periphery thereof and fired at a temperature of approx. 450° C. for 10 to 20 min., for example, to from hermetical seal layer 121 (see FIG. 1) for sealing. Next, discharge space 122 is once evacuated to a high vacuum (e.g. 1.1×10⁻⁴ Pa) and filled with a discharge gas (e.g. He—Xe or Ne—Xe inert gas) at a specified pressure, to provide PDP 100.

(4) A method of Forming Phosphor Layers

FIG. 5 is a schematic diagram showing a structure of ink dispenser 200 for use in forming phosphor layers 110R, 110G, and 110B. As shown in FIG. 5, ink dispenser 200 includes server 210, pressure pump 220, and header 230. Phosphor ink is pressurized by pressure pump 220 and supplied from server 210 for storing the phosphor ink to header 230.

The ink dispenser is structured so that header 230 has ink chamber 230 a and nozzle 240, and the phosphor ink pressurized and supplied to ink chamber 230 a is continuously ejected from nozzle 240. It is desirable that bore diameter D of this nozzle 240 is set to at least 30 μm in order to prevent clogging of the nozzle. It is also desirable that bore diameter D is equal to or smaller than interval W between barrier ribs 109 (approx. 130 to 200 μm) in order to prevent displacement of a phosphor layer from the barrier ribs in application. Thus, bore diameter D is generally set to 30 to 130 μm.

Header 230 is structured to be driven lineally by a header scanning mechanism (not shown). Continuously ejecting phosphor ink 250 from nozzle 240 and scanning header 230 at the same time allows the phosphor ink to be uniformly applied to the grooves between barrier ribs 109 on rear glass substrate 102. Viscosity of the phosphor ink used in this embodiment is kept within the range of 1,500 to 3,000 centipoises (CP) at a temperature of 25° C.

This server 210 also has a mixer (not shown). Mixing prevents precipitation of particles in phosphor ink. Header 230 is integrally formed with ink chamber 230 a and nozzle 240 by performing machining and electric discharge machining on a metallic material.

The methods of forming phosphor layers are not limited to the above method. Other various kinds of usable methods include photolithography, screen-printing, and a method of disposing a film including phosphor particles mixed therein.

The phosphor ink is prepared by mixing phosphor particles of each color, a binder and a solvent so that the mixture has a viscosity ranging from 1,500 to 3,000 centipoises (CP). A surface-active agent, silica, a dispersant agent (0.1 to 5 wt %) can also be added, as required.

Used as a red phosphor included in this phosphor ink is a compound represented by (Y,Gd)_(1−x)BO₃:Eu_(x) or Y_(2−x)O₃:Eu_(x). In these compounds, the element Eu substitutes for part of the element Y constituting the matrix of the compounds. It is preferable that the substitution value X of the element Eu with respect to the element Y is 0.05≦X≦0.20. For a substitution value larger than this value, the phosphor has a high luminance but considerable luminance degradation. For this reason, it is considered that the red phosphor cannot be used practically. For a substitution value smaller than this value, the composition ratio of Eu mainly emitting light is small and thus the luminance decreases. Therefore, the red phosphor cannot be used as a phosphor.

Used as a green phosphor is a compound represented by Ba_(1−x)Al₁₂O₁₉: Mn_(x) or Zn_(2−x)SiO₄:Mn_(x). Ba_(1−x)Al₁₂O₁₉:Mn_(x) is a compound in which the element Mn substitutes for part of the element Ba constituting the matrix of the compound. Zn_(2−x)SiO₄:Mn_(x) is a compound in which the element Mn substitutes for part of the element Zn constituting the matrix of the compound. It is preferable that the substitution value X of the element Mn with respect to the elements Ba and Zn is 0.01≦X≦0.10 for the reason described in the case of the red phosphor.

Used as a blue phosphor is a compound represented by Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) or Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x). Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x) are compounds in which divalent Eu and/or divalent Sr substitute for part of the element Ba constituting the matrix of the compounds. It is preferable that the substitution value X of the element Eu and substitution value Y of the element Sr with respect to the element Ba are 0.03≦X≦0.20 and 0.1≦Y≦0.5, respectively, for the reason described in the case described above.

It is also preferable that the substitution value of trivalent Eu ions substituting for the divalent Eu ions is 0.001≦a≦0.15, in BaEu(+2)_(1−a)Eu(+3)_(a)MgAl₁₀O₁₇:Eu. In other words, it is preferable that the substitution value ranges from 0.1 to 15%.

Ethyl cellulose or acrylic resin can be used as a binder included in phosphor ink (in an amount of 0.1 to 10 wt % of the ink) and α-terpineol or n-butylcarbitol can be used as a solvent. Polymers, such as PMA and PVA, can also be used as a binder, and organic solvent, such as diethyleneglycol and methyl ether, can also be used as a solvent.

The phosphor particles used in this embodiment are manufactured by a solid-phase firing method, aqueous solution reaction method, spray firing method, or hydrothermal synthesis method.

(1) Blue Phosphor

Ba_(1−x)MgAl₁₀O₁₇:Eu_(x)

First, in a mixed solution fabrication process, materials, i.e. barium nitrate (Ba(NO₃)₂) , magnesium nitrate (Mg(NO₃)₂), aluminum nitrate (Al(NO₃)₃) , and europium nitrate (Eu(NO₃)₂) are mixed in a molar ratio of Ba(NO₃)_(2:)Mg(NO₃)₂:Al(NO₃)₃:Eu(NO₃)₂=1−X:1:10:X (0.03≦X≦0.25). This mixture is dissolved in an aqueous medium to provide a mixed solution. As this aqueous medium, ion-exchange water or pure water is preferable because they contain no impurities. However, non-aqueous solvent (e.g. methanol and ethanol) can be contained in the aqueous medium.

Next, the hydrate mixed solution is held in a container made of a corrosion- and heat-resistant material, such as gold and platinum. Then the mixed solution is hydro-thermally synthesized in a high pressure vessel, using equipment capable of heating and pressurizing at the same time, such as an autoclave, for 12 to 20 hours, at specified temperatures (100 to 300° C.) under specified pressures (0.2 to 10 MPa).

Next, the obtained particles are fired in a reducing atmosphere containing 5% of hydrogen and 95% of nitrogen, for example, at a specified temperature for a specified period (e.g. at 1,350° C. for two hours). Thereafter, the fired particles are classified and fired in O₂, O₂—N₂, or O₃—N₂, for 350 to 900° C., to provide a desired blue phosphor, Ba_(1−x)MgAl₁₀O₁₇:Eu_(x). In this blue phosphor, trivalent Eu ions have substituted for part of divalent Eu in the blue phosphor fabricated in the reducing atmosphere (most of Eu ions in the latter blue phosphor being divalent).

When the particles are fired in O₂, O₂—N₂, or O₃−N₂, degradation characteristics of the blue phosphor can further be inhibited by attaching an oxide, e.g. Al₂O₃, SiO₂, and La₂O₃, and a fluoride, e.g. LaF₂ and ALF_(3,) to the surface of the phosphor, using an organic compound containing these elements, e.g. alkoxide, acetylacetone, and organic silane, by hydrolysis (a method of mixing the phosphor particles, an organic solvent, e.g. alcohol, and an organic compound, hydrolyzing the organic compound on the surface of the phosphor, and thereafter removing the alcohol or other organic solvent and firing). It is preferable that the thickness of these oxide and fluoride is as small as possible so that ultraviolet light could pass through the particles. In other words, preferably, it is up to 0.1 μm.

The phosphor particles obtained by hydrothermal synthesis have spherical shapes and an average particle diameter ranging from approx. 0.05 to 2.0 μm, which is smaller than that of particles fabricated by the conventional solid-phase reaction method. Now, the term “spherical” as used herein is defined so that the aspect ratios (minor axis diameter/major axis diameter) of most of the phosphor particles range from 0.9 to 1.0, for example. Not all the phosphor particles need to fall within this range.

The hydrate mixture can be sprayed from a nozzle into a high-temperature furnace to synthesize a phosphor instead of being held in a gold or platinum container. A blue phosphor subjected to substitution can also be fabricated by firing a blue phosphor obtained by this spray method in O₂, O₂—N₂, or O₃—N₂.

Ba_(1−x−y)Sr_(y)Al₁₀O₁₇:Eu_(x)

This phosphor is made of materials different from those of the above Ba_(1−x)MgAl₁₀O₁₇:Eu_(x,) and fabricated by a solid reaction method. The materials used are described hereinafter.

The materials, i.e. barium hydroxide (Ba(OH)₂), strontium hydroxide (Sr(OH)₂), magnesium hydroxide (Mg(OH)₂), aluminum hydroxide (Al(OH)₃), and europium hydroxide (Eu(OH)₂) are weighted in a required molar ratio. These materials are mixed together with AlF₃, a fluxing agent. The mixture is fired in a reducing atmosphere (5% of hydrogen and 95% of nitrogen, for example) at specified temperatures (1,000 to 1,600° C.) for two hours and then classified by an air classifier, to provide blue phosphor particles. Thereafter, the blue phosphor particles are fired in O₂, O₂—N₂, or O₃—N₂ to provide a blue phosphor in which trivalent ions substitute for divalent Eu ions.

Mainly used as the materials of the phosphor are oxides, nitrates, or hydroxides. However, the phosphor can also be fabricated using organometallic compounds containing Ba, Sr, Mg, Al, Eu and other elements, such as metal alkoxide and acetylacetone. Further, when a phosphor is fired in O₂, O₂—N₂, or O₃—N₂, degradation characteristics of the phosphor can be inhibited by coating it with materials, such as Al₂O₃, SiO₂, ALF₃, La₂O₃, and LaF₂, by hydrolysis using metal alkoxide or acetylacetone, at the same time

(2) Green Phosphor

Zn_(2−x)SiO₄:Mn_(x)

First, in a mixed solution fabrication process, materials, i.e. zinc nitrate (Zn(NO₃)), silicon nitrate (Si(NO₃)₂), and manganese nitrate (Mn(NO₃)₂) are mixed in a molar ratio of Zn(NO₃):Si(NO₃)₂:Mn(NO₃)₂=2−X:1:X(0.01≦X≦0.10). Next, this mixed solution is sprayed from a nozzle into a furnace heated to a temperature of 1,500° C. while ultrasonic waves are applied thereto. Thus, the green phosphor is fabricated.

Ba_(1−x)Al₁₂O₁₉:Mn_(x)

First, in a mixed solution fabrication process, materials, i.e. barium nitrate (Ba(NO₃)₂), aluminum nitrate (Al(NO₃)₂), and manganese nitrate (Mn(NO₃)₂), are mixed in a molar ratio of Ba(NO₃)₂:Al(NO₃)₂:Mn(NO₃)₂ =1−X:12:X(0.01≦X≦0.10). This mixture is dissolved in ion-exchange water to provide a mixed solution.

Next, in a hydration process, an aqueous base (e.g. ammonia aqueous solution) is dropped into this mixed solution to form a hydrate. Thereafter, in a hydrothermal synthesis process, this hydrate and ion-exchange water is held in a capsule made of a corrosion- and heat-resistant material, such as platinum and gold. This solution is hydro-thermally synthesized at specified temperatures under specified pressures for specified periods of time (e.g. 100 to 300° C., 0.2 to 10 MPa, 2 to 20 hours) in a high pressure vessel, using an autoclave, for example.

Thereafter, the compound is dried to provide a desired Ba_(1−x)Al₁₂O₁₉:Mn_(x). The phosphor obtained by this hydrothermal synthesis process has particle diameters ranging from approx. 0.1 to 2.0 μm and spherical shapes. Next, these particles are annealed in air at temperatures ranging from 800 to 1,100° C., and classified to provide the green phosphor.

(3) Red Phosphor

(Y,Gd)_(1−x)BO₃:Eu_(x)

First, in a mixed solution fabrication process, materials, i.e. yttrium nitrate (Y₂(NO₃)₂) , hydro nitrate gadolinium (Gd₂(NO₃)₃), boric acid (H₃BO₃) , and europium nitrate (Eu₂(NO₃)₃) are mixed in a molar ratio as an oxide of 1−X:2:X (0.05≦X≦0.20) and a ratio of Y:Gd=65:35. Next, this mixed solution is heat-treated in air at temperatures ranging 1,200 to 1,350° C. for two hours and classified to provide the red phosphor.

Y_(2−x)O₃:Eu_(x)

First, in a mixed solution fabrication process, materials, i.e. yttrium nitrate (Y₂(NO₃)₂) and europium nitrate (Eu(NO₃)₂) are mixed in a molar ratio of Y₂(NO₃)₂: Eu(NO₃)₂=2−X:X (0.05≦X≦0.30). This mixture is dissolved in ion-exchange water to provide a mixed solution.

Next, in a hydration process, an aqueous base (e.g. ammonia aqueous solution) is added to this mixed solution to provide a hydrate.

Thereafter, in a hydrothermal synthesis process, this hydrate and ion-exchange water is held in a container made of a corrosion-and heat-resistant material, such as platinum and gold. This mixture is hydro-thermally synthesized at temperatures ranging from 100 to 300° C., under pressures ranging from 0.2 to 10 MPa, for 3 to 12 hours, in a high pressure vessel, using an autoclave, for example. Then, the obtained compound is dried to provide a desired Y_(2−x)O₃:Eu_(x).

Next, this phosphor is annealed in air at temperatures ranging from 1,300 to 1,400° C. for two hours, and classified to provide the red phosphor. The phosphor obtained by this hydrothermal synthesis process has particle diameters ranging from approx. 0.1 to 2.0 μm and spherical shapes. These particle diameters and shapes are suitable for forming a phosphor layer having excellent light emission characteristics.

Conventional phosphors are used for phosphor layers 110R and 110G of PDP100 described above. Used for phosphor layer 110B are phosphor particles in which trivalent Eu ions substitute for part of divalent Eu ions constituting the phosphor. Especially, the conventional blue phosphor has more degradation than the blue phosphor of the present invention in each process; thus, the color temperature of white tends to decrease when the three colors emit light at the same time.

For this reason, in a plasma display device, the color temperature of white display has been improved by decreasing the luminance of phosphor cells of colors other than blue (i.e. red and green), using circuits. However, the use of a blue phosphor of the present invention increases the luminance of blue cells and decreases luminance degradation in the panel manufacturing process. This eliminates the need of intentionally decreasing the luminance of the cells of other colors and thus the need of intentionally decreasing the luminance of the cells of all the colors. Therefore, because the luminance of the cells of all the colors can fully be utilized, the luminance of the plasma display device can be increased while the color temperature of white display is kept high.

The blue phosphor of the present invention can be applied to fluorescent lighting that is excited by ultraviolet light to emit light in a similar manner. In this case, a phosphor layer including conventional blue phosphor particles that is applied to the inner wall of a fluorescent tube is replaced with a phosphor layer including a blue phosphor in which trivalent Eu ions substitute for divalent Eu ions.

Application of the present invention to fluorescent lighting in this manner can provide fluorescent lighting having a luminance and resistance to luminance degradation more excellent than those of conventional fluorescent lighting.

In order to evaluate the performance of a plasma display device of the present invention, samples based on the preferred embodiment were produced and performance evaluation tests were performed on the samples. The experimental results are described below.

Each of the plasma display devices was produced to have a diagonal size of 42 inch. (HDTV screen having a rib pitch of 150 μm). Each of the plasma display devices was produced so that the dielectric glass layer was 20 μm thick, the MgO protective layer was 0.5 μm thick, and the distance between the display electrode and the display scan electrode was 0.08 mm. The discharge gas charged into the discharge space essentially consists of neon and contains 5% of xenon gas mixed therein.

In the blue phosphor particles of each of Sample Nos. 1 through 10 used for the plasma display devices, trivalent Eu ions substitute for divalent Eu ions constituting each phosphor. The synthesis conditions of each sample are shown in Table 1.

TABLE 1 Ratio of triva- lent Eu to Manu- Sam- Amount Method of diva- Amount Amount facturing ple of Eu Manufacturing substituting trivalent lent Coating of Eu Manufacturing of Mn meth- No. x, y method Eu for divalent Eu Eu layer X method X od Red phosphor Green phosphor Blue phosphor [Ba_(1−x)MgAl₁₀O₁₇:Eu_(x)] [(Y, Gd)_(1−x)BO₃:Eu_(x)] [Zn_(2−x)SiO₄:Mn_(x)]  1 X = Hydrothermal synthesis Oxidation in O₂, at 0.001 Al₂O₃ X = 0.1 Solid-phase X = 0.01 Spray method 0.03 method 500° C., for 10 min. Reaction method  2 X = Solid-phase reaction Oxidation in O₂, at 0.005 SiO₂ X = 0.2 Spray method X = 0.02 Hydrothermal 0.05 method (Flux method) 600° C., for 10 min. synthesis method  3 X = Spray method Oxidation in 0.03 La₂O₃ X = 0.3 Aqueous solution X = 0.05 Solid-phase 0.1 N₂—O₂ (10%), at reaction method Reaction 700° C., for 60 min. method  4 X = Aqueous solution Oxidation in 0.15 LaF₃ X = 0.15 Hydrothermal X = 0.1 Solid-phase 0.2 reaction method N₂—O₂ (20%), at synthesis method Reaction 900° C., for 30 min. method Green phosphor Blue phosphor [Ba_(1−x−y)Sr_(y)Al₁₀O₁₇:Eu_(x)] Red phosphor [Y_(2−x)O₃:Eu_(x)] [Ba_(1−x)Al₁₂O₁₉:Mn_(x)]  5 X = Solid-phase reaction Oxidation in N₂—O₃ 0.015 SiO₂ X = 0.01 Hydrothermal X = 0.01 Hydrothermal 0.03 method (Flux method) (3%), at 350° C., for synthesis method synthesis y = 10 min. method 0.1  6 X = Hydrothermal synthesis Oxidation in N₂—O₃ 0.05 AlF₃ X = 0.1 Spray method X = 0.02 Spray method 0.1 method (2%), at 600° C., for y = 10 min. 0.3  7 X = Spray method Oxidation in N₂—O₃ 0.145 None X = 0.15 Aqueous solution X = 0.05 Solid-phase 0.1 (1%), at 700° C., for reaction method Reaction y = 30 min. method 0.5  8 X = Solid-phase reaction Oxidation in 0.056 None X = 0.2 Solid-phase X = 0.1 Solid-phase 0.2 method N₂—O₂ (20%), at Reaction method Reaction y = 700° C., for 15 min. method 0.3  9 X = Solid-phase reaction Oxidation in N₂—O₂ 0.002 None ″ Solid-phase ″ Solid-phase 0.2 method (5%), at 700° C., for Reaction method Reaction y = 15 min. method 0.3  10 X = Solid-phase reaction Oxidation in N₂—O₂ 0.051 None X = 0.15 Aqueous solution X = 0.01 Hydrothermal 0.1 method (1%), at 900° C., for reaction method synthesis y = 10 min. method 0.5 *11 X = Solid-phase reaction None None None ″ Aqueous solution ″ Hydrothermal 0.1 method reaction method synthesis y = method 0.5 *Sample No. 11 shows a comparative example.

With reference to Table 1, for each of Sample Nos. 1 through 4, (Y,Gd)_(1−x)BO₃:Eu_(x) red phosphor, Zn_(2−x)SiO₄:Mn_(x) green phosphor, and Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) blue phosphor are used in combination. The method of synthesizing the phosphors, the substitution ratios of Eu and Mn mainly emitting light, (i.e. the substitution ratios of Eu to the elements Y and Ba and the substitution ratio of Mn to the element Zn), and the amount of trivalent Eu ions substituting for divalent Eu ions are changed as shown in Table 1. In each of the blue phosphors of Sample Nos. 1 through 4, particles are coated with an oxide or a fluoride, by hydrolysis using metal alkoxide or acetylacetone containing the coating element.

For each of Sample Nos. 5 through 10, Y_(2−x)O₃:Eu_(x) red phosphor, Ba_(1−x)Al₁₂O₁₉:Mn_(x) green phosphor, and Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x) blue phosphor are used in combination. Similar to the above cases, the conditions for the method of synthesizing the phosphors, the substitution ratios of the elements mainly emitting light, and the amount of trivalent Eu ions substituting for divalent Eu ions constituting the blue phosphor are changed as shown in Table 1. In each of Sample Nos. 5 and 6, particles are coated with an oxide or a fluoride by hydrolysis.

Phosphor ink used for forming a phosphor layer is prepared by using each kind of phosphor particles shown Table 1, and mixing the phosphor, a resin, solvent and dispersion agent. According to the measurement results, viscosity of each kind of the phosphor ink (at 25° C.) is kept within the range of 1,500 to 30,000 CP. According to observations of each phosphor layer formed, the phosphor ink is uniformly applied to the side faces of the barrier ribs.

As for the phosphor particles used for a phosphor layer of each color, those having an average diameter ranging from 0.1 to 3.0 μm and a maximum diameter up to 8 μm are used in each sample.

Sample No. 11 shows a comparative example using conventional phosphor particles in which no special treatment is performed on the phosphor particles of each color.

The divalent and trivalent Eu ions in Table 1 are measured by a cathode luminescence analysis (accelerating voltage: 1 KV).

Experiment 1

Model experiments were performed on Sample Nos. 1 through 10 and Sample No. 11 (a comparative example) to determine luminances and luminance degradation factors. In the model experiments, these phosphors were fired (520° C., 20 min.) in the rear panel manufacturing process to determine how the luminance of each color changed. The luminance of the particles before firing and the luminance of the applied paste after firing were measured. The luminance degradation factor of each color before and after firing was measured.

Experiment 2

Measured was the luminance degradation factor of each phosphor before and after the panel assembly step (sealing at 45° C. for 20 min.) in the panel manufacturing process.

Experiment 3

When each panel was lit in each color, a luminance and luminance degradation factor were measured as follows. Discharge sustain pulses at a voltage of 200V and at a frequency of 100 kHz were applied to each plasma display device continuously for 100 hours, luminances of each panel was measured before and after the application of the pulses, and a luminance degradation factor (([luminance after application−luminance before application]/luminance before application)*100) was determined.

Addressing failure at address discharge was determined by existence of flickers in an image. If flickers were found even only in one position, it was recognized as having flickers. As for the luminance distribution of each panel, a luminance was measured with a luminance meter when white color was displayed and the distribution on the entire surface was shown.

Shown in Table 2 are results of the luminances and the luminance degradation factors of each color in these experiments 1 through 3.

TABLE 2 Luminance Luminance Luminance degradation factor degradation degradation (%) of phosphor af- factor (%) of phosphor factor (%) of phosphor ter application of dis- Existence of Luminance at fired (520° C.) in rear when panels are sealed charge sustain pulses addressing blue display panel manufacturing (450° C.) in panel (200 V, 100 kHz, failure at on the entire Sample process assembly process 100 hours) address surface No. Blue Red Green Blue Red Green Blue Red Green discharge cd/cm²  1 −0.1 −1.2 −4.9 −0.5 −2.6 −13.0 −1.5 −4.4 −14.5 Not exist 86.1  2 −0.2 −1.3 −4.0 −0.3 −2.4 −13.2 −1.3 −4.1 −14.2 ″ 85.7  3 −0.2 −1.4 −4.5 −0.4 −2.3 −12.9 −1.4 −4.0 −14.6 ″ 88  4 −0.2 −1.4 −4.7 −0.3 −2.2 −12.7 −1.0 −4.2 −14.1 ″ 85  5 −0.1 −1.5 −4.9 −0.2 −2.0 −12.9 −1.2 4.3 −14.8 ″ 87.9  6 −0.2 −1.2 −4.3 −0.3 −2.3 −12.6 −1.1 −4.1 −14.9 ″ 91  7 −0.4 −1.4 −4.5 −1.1 −2.4 −12.3 −2.4 −4.2 −14.7 ″ 86.9  8 −0.3 −1.2 −4.3 −1.5 −2.5 −12.5 −2.1 −4.3 −15.1 ″ 90.5  9 −0.4 −1.5 −4.1 −1.2 −2.1 −12.8 −2.5 −4.1 −15.6 ″ 92.3  10 −0.5 −1.3 −4.2 −1.4 −2.3 −13.0 −1.6 −4.1 −14.8 ″ 91.8 *11 −5.5 −1.5 −4.1 −21.5 −2.1 −13.2 −35 −4.1 −15.6 Exist 45.8 *Sample No. 11 shows a comparative example.

As shown in Table 2, for Sample No. 11 in which no trivalent Eu ions have substituted for divalent Eu ions in the blue phosphor, the luminance degradation factors in each process are large. Especially for the blue phosphor, a luminance degradation factor of 5.5% is seen in the phosphor firing process, 21.5% in the sealing process, and 35% in the acceleration life test (200V, 100 kHz). In contrast, for Sample Nos. 1 through 10, all the degradation factors of the blue phosphors are up to 2.5%. Additionally, no addressing failure is found.

This is because trivalent Eu ions have substituted for part of divalent Eu ions constituting each blue phosphor and this substitution has drastically reduced oxygen vacancy in the blue phosphor (especially oxygen vacancy in the vicinity of Ba—O layers). This prevents defective layers (oxygen vacancy in the vicinity of the Ba—O layers) on the surface of the phosphor from adsorbing water included in the ambient atmosphere in firing the phosphor or water in MgO, barrier ribs, sealing frit, and the phosphors in sealing panels.

Experiment 4

Model experiments were performed on phosphors in which no trivalent Eu ions had substituted for part of divalent Eu ions in blue phosphors thereof. The phosphors were left in an atmosphere at a temperature of 60° C. and a relative humidity of 90% for 10 min., and dried at a temperature of 100° C. Then, temperature-programmed desorption gas chromatograph-mass spectrometry (TDS analysis) was performed on these phosphors. The analysis results show that the peaks of physically adsorbed water (approx. 100° C.) and chemically adsorbed water (300 to 500° C.) are 12 times as high as those in the samples subjected to substitution (Sample Nos. 1 through 10).

Experiment 5

Shown in the Experiment 1 are examples in which blue phosphors of the present invention are used in PDPs. A sample of fluorescent lighting using a phosphor of the present invention in which trivalent Eu ions substitute for part of divalent Eu ions in a blue phosphor thereof was produced for fluorescent lighting excited by ultraviolet light to emit light, in a similar manner.

Phosphors of respective colors produced under the condition of Sample No. 7 of Table 1 were mixed and the mixture was applied to the inner wall of a glass tube, as a phosphor layer of known fluorescent lighting, to provide Sample No. 12. As a comparative example thereof, phosphors of respective colors produced by conventional solid-phase reaction under the condition of Sample No. 11 (of Table 1) without substitution were also mixed and applied as a phosphor layer, to provide Sample No. 13, comparative fluorescent lighting. Table 3 shows the results.

TABLE 3 Sample Luminance Luminance degradation after No. Phosphor (cd/m²) 5,000 hours (100 V, 60 Hz) 12 Phosphor of 6,750 −1.00% Sample No. 7 13* Phosphor of 6,600 −14.6% Sample No. 11 *Sample No. 13 shows a comparative example

INDUSTRIAL APPLICABILITY

As described above, in accordance with the present invention, substituting trivalent Eu ions for part of divalent Eu ions in the crystal of a blue phosphor constituting a phosphor layer can prevent degradation of the phosphor layer in each manufacturing process. This method can improve luminance, life and reliability of a panel and a lamp. 

1. A plasma display device having a plasma display panel in which a plurality of discharge cells having one of one color and a plurality of colors are disposed, phosphor layers having a color corresponding to said respective discharge cells are disposed in arrays, and said phosphor layers are excited by ultraviolet light to emit light, wherein said phosphor layers have a blue phosphor, and said blue phosphor is selected from a group of compounds consisting of Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), wherein part of a divalent Eu ion constituting said phosphor is made trivalent in an oxidizing atmosphere, the amount of the trivalent Eu ion ranges from 0.1 to 15% of the divalent ion, and wherein 0.03≦x≦0.20 and 0.1≦y≦0.5.
 2. A blue phosphor excited by ultraviolet light to emit visible light comprising a crystal structure selected from a group consisting of Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), wherein part of a divalent Eu ion constituting said phosphor is made trivalent in an oxidizing atmosphere, the amount of the trivalent Eu ion ranges from 0.1 to 15% of the divalent ion, and wherein 0.03≦x≦0.20 and 0.1≦y≦0.5.
 3. A method of manufacturing a phosphor comprising the step of: making a blue phosphor having a divalent Eu ion as a matrix thereof selected from a group consisting of Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), where 0.03≦x≦0.20 and 0.1≦y≦0.5 and then firing the blue phosphor in an oxidizing atmosphere, to make part of a divalent Eu ion trivalent, the amount of the trivalent Eu ion ranges from 0.1 to 15% of the divalent ion.
 4. The method of manufacturing a phosphor of claim 3, wherein, in said firing step, the oxidizing atmosphere is one of oxygen, oxygen-nitrogen, and ozone-nitrogen, and firing temperatures range from 350 to 900° C.
 5. A plasma display device having a plasma display panel in which a plurality of discharge cells having one of one color and a plurality of colors are disposed, phosphor layers having a color corresponding to said respective discharge cells are disposed in arrays, and said phosphor layers include a blue phosphor selected from a group of compounds consisting of Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), where 0.03≦x≦0.20 and 0.1 y≦0.5, said blue phosphor fired in an oxidizing atmosphere to convert 0.1 to 15% of the divalent Eu ions to trivalent Eu ions.
 6. A blue phosphor obtained after matrix selected from a group consisting of Ba_(1−x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1−x−y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), is fired in an oxidizing atmosphere, wherein 0.1 to 15% of the Eu ions in the oxidized matrix are divalent and the remainder of the Eu ions in the oxidized matrix are trivalent, and wherein 0.03≦x≦0.20 and 0.1≦y≦0.5. 